8030-T6
...
8030-O
...
6008-T5
Density2.70g/cm3Density2.71 g/cm3 (169 lb/ft3)Elastic (Young's, Tensile) Modulus70 GPa (10 x 106 psi)Elongation at Break10 to 17 %Specific Heat Capacity890 J/kg-KStrength to Weight Ratio74 to 111 kN-m/kgTensile Strength: Ultimate (UTS)200 to 300 MPa (29 to 44 x 103 psi)Tensile Strength: Yield (Proof)100 to 240 MPa (15 to 35 x 103 psi)Thermal...
6005-AT5
Density2.72g/cm3Density2.71 g/cm3 (169 lb/ft3)Elastic (Young's, Tensile) Modulus70 GPa (10 x 106 psi)Electrical Conductivity50 % IACSElongation at Break11 %Melting Onset (Solidus)605 °C (1120 °F)Shear Modulus26 GPa (3.8 106 psi)Specific Heat Capacity890 J/kg-KStrength to Weight Ratio103 kN-m/kgTensile Strength: Ultimate (UTS)280 MPa (41 x 103...
5083-H321
Density2.66 g/cm3 (166 lb/ft3)Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi)Electrical Conductivity29 % IACSElongation at Break15 %Melting Onset (Solidus)574 °C (1070 °F)Shear Modulus27 GPa (3.9 106 psi)Specific Heat Capacity900 J/kg-KStrength to Weight Ratio128 kN-m/kgTensile Strength: Ultimate (UTS)340 MPa (49 x 103 psi)Tensile...
7050-T7452
Density2.80 g/cm3 (175 lb/ft3)Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi)Elongation at Break8 to 9 %Specific Heat Capacity800 J/kg-KStrength to Weight Ratio193 to 196 kN-m/kgTensile Strength: Ultimate (UTS)540 to 550 MPa (78 to 80 x 103 psi)Tensile Strength: Yield (Proof)450 to 460 MPa (65 to 67 x 103 psi)Thermal Expansion22.1...
7020-T4
Density2.78 g/cm3 (174 lb/ft3)Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi)Elongation at Break15 %Melting Onset (Solidus)605 °C (1120 °F)Shear Modulus26 GPa (3.8 106 psi)Specific Heat Capacity870 J/kg-KStrength to Weight Ratio129 kN-m/kgTensile Strength: Ultimate (UTS)360 MPa (52 x 103 psi)Tensile Strength: Yield (Proof)240 MPa (35 x...
5083-H112
Density2.66 g/cm3 (166 lb/ft3)Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi)Electrical Conductivity29 % IACSElongation at Break16 %Melting Onset (Solidus)574 °C (1070 °F)Shear Modulus27 GPa (3.9 106 psi)Specific Heat Capacity900 J/kg-KStrength to Weight Ratio113 kN-m/kgTensile Strength: Ultimate (UTS)300 MPa (44 x 103 psi)Tensile...
5083-O
Density2.66 g/cm3 (166 lb/ft3)Elastic (Young's, Tensile) Modulus71 GPa (10 x 106 psi)Electrical Conductivity29 % IACSElongation at Break17 %Fatigue Strength (Endurance Limit)150 MPa (22 x 103 psi)Melting Onset (Solidus)574 °C (1070 °F)Shear Modulus27 GPa (3.9 106 psi)Shear Strength172 MPa (25 x 103 psi)Specific Heat Capacity900 J/kg-KStrength to...
7075-T6
Density2.80 g/cm3 (175 lb/ft3)Elastic (Young's, Tensile) Modulus72 GPa (10 x 106 psi)Electrical Conductivity33 % IACSElongation at Break10 %Fatigue Strength (Endurance Limit)160 MPa (23 x 103 psi)Melting Onset (Solidus)477 °C (891 °F)Shear Modulus27 GPa (3.9 106 psi)Shear Strength331 MPa (48 x 103 psi)Specific Heat Capacity960 J/kg-KStrength to...